6013 aluminium alloy
Alloy of aluminum
6013 aluminium alloy consist of magnesium, silicon, copper, manganese, iron, zinc, chromium, and titanium as minor alloying elements.[1]
Chemical Composition
Element [1] | Weight percentage (%) |
---|---|
Aluminum, Al | 94.8-97.8 |
Magnesium, Mg | 0.80-1.2 |
Silicon, Si | 0.60-1 |
Copper, Cu | 0.60-1.1 |
Manganese, Mn | 0.20-0.80 |
Iron, Fe | ≤ 0.50 |
Zinc, Zn | ≤ 0.25 |
Chromium, Cr | ≤ 0.10 |
Titanium, Ti | ≤ 0.10 |
Remainder (each) | ≤ 0.15 |
Remainder (total) | ≤ 0.050 |
Mechanical Properties
Properties [1] | Values |
---|---|
Tensile strength | ≥ 392 MPa |
Yield strength | ≥ 379 MPa |
Elongation at break | ≥ 5% |
Young's Modulus [2] | 69 GPa |
Fatigue Strength [2] | 98 to 140 MPa |
Applications
- Valves
- Machine parts
- Munitions
- ABS Braking systems
- Hydraulic applications
- Roller blade parts
[1]
References
- ^ a b c d "6013 aluminium alloy properties". 25 April 2013. Archived from the original on 2016-09-14.
- ^ a b "6013 Aluminium alloy properties". Archived from the original on 2016-11-14.
- v
- t
- e
Aluminium alloys
- Aluminium
- Aluminium alloys
- History of aluminium
- 4006
- 4007
- 4015
- 4032
- 4043
- 4047
- 4543
- Aluminium–lithium alloys
- AlBeMet
- Alclad
- Alnico
- AlSiC
- Alumel
- Aluminium granules
- Alusil
- Birmabright
- Devarda's alloy
- Duralumin
- Hiduminium (aka R.R. alloys)
- Hydronalium
- Italma
- Lo-Ex
- Magnalium
- Magnox (alloy)
- MKM steel
- Nickel aluminide
- Aluminium–scandium alloys
- Y alloy
- Al-Ca composite
- Hypereutectic piston
- Aluminium bronze
- AlSi10Mg